A kind of stable cationic polymer emulsion is prepared with soap-free emulsion, cationic monomer and initiator by radicalcopolymerization.
采用无皂乳液聚合,选择合适的阳离子单体和引发剂,用自由基聚合法合成了稳定的阳离子型聚合物乳液。
First use soap-free emulsion preparation for polystyrene spheres, and the kernel, Reuse are silicon acetic tetraethyl ortho-silicate in ammonia catalytic hydrolysis, formed under the condition of silica, charged by six water or their cerium, six of methylene amine solution HMT (4) into the negatively charged, uniform cerium oxide coated surfaces to PS microspheres, core-shell structure of PS - CeO2 and PS - SiO2 composite microspheres.
首先用无皂乳液制备了聚苯乙烯微球,并以此为内核;再利用正硅乙酸乙酯在氨水催化条件下水解,形成带负电性的二氧化硅,或者利用六水亚硝酸铈、六亚甲基四胺水溶液分解出带负电性的氧化铈,均匀的包覆到PS微球表面,形成核-壳结构的PS-CeO2和PS-SiO2复合微球。
Monodisperse poly (styrene-co-acrylic acid) latexes with carboxylic surface are synthesized by soap - free emulsion polymerization.
利用无皂乳液聚合法合成了表面富含羧基的单分散聚(苯乙烯-共-丙烯酸)乳胶粒子模板。
Studies on the Soap-Free Emulsion Copolymerization of Methyl Methacrylate and N-hydroxymethyl Acrylamide
甲基丙烯酸甲酯/羟甲基丙烯酰胺无皂乳液共聚合的研究
Study on Soap-Free Acrylic Resin/Nano-SiO_2 Emulsion Compound Coatings for Leather
无皂丙烯酸树脂/SiO2纳米复合皮革涂饰剂的研究
Studies on styrene/butylacrylate/n, n dimethyl n butyl n methacryl oxyethyl ammonium bromide soap free cationic emulsion
苯乙烯/丙烯酸丁酯/(二甲基丁基)甲基丙烯酰氧乙基溴化铵无皂阳离子乳液研究
Preparation and application of a soap-free emulsion based on styrene acrylate and anthraquinone composite
无皂苯丙聚合物分散蒽醌复合乳液的制备与应用
A soap-free poly (styrene/butylacrylate) P (St/BA) emulsion was prepared in the presence of the sodium salt of methacrylic acid.
在少量甲基丙烯酸钠盐的存在下,成功合成了具有高稳定性、高透明性的聚(苯乙烯/丙烯酸丁酯)P(St/BA)无皂共聚乳液。
Poly (methyl methacrylate - co-methacrylic acid)/polystyrene (P (MMA - MAA)/PS) composite particles with microvoid morphology were prepared by soap-free seeded emulsion polymerization.
采用无皂种子乳液聚合制备了具有微空腔形态的聚(甲基丙烯酸甲酯共甲基丙烯酸)/聚苯乙烯〔P(MMA-MAA)/PS〕复合微粒并讨论了形态形成原理。
In this paper, antimicrobial polymer microsphere is prepared by one stage soap-free emulsion copolymerization.
本论文采用无皂乳液聚合的方法,经一步聚合过程成功的制备了表面键接抗菌基团的聚合物微球。
Prepared antimicrobial polymer microsphere by soap-free emulsion polymerization in the presence of functional monomer synthesized by 1. And characterized their morphology by electron microscopy, characterized their shell composition by XPS, characterized their size and distribution by electron microscopy and particle size analysis instrument. 3.
在功能单体存在下进行无皂乳液聚合,制备抗菌聚合物微球,并用电镜表征其形貌、用XPS表征其表层物质的组成、用电镜和粒度分析仪表征其粒径大小及分布。
In this paper the soap-free emulsion copolymerization of methyl methacrylate and N-hydroxymethyl acrylamide was studied, using potassium persulfate (K 2S 2O 8) as initiator.
以甲基丙烯酸甲酯为主单体、N-羟甲基丙烯酰胺为功能性单体、K2S2O8为引发剂进行了无皂乳液共聚合的研究;
This article has described the soap-free copolymerization with vinyl acetate (VAc) as basic monomer and acrylic acid (AA) as modification functional monomer, forming a stable emulsion with 30% solid.
以醋酸乙烯(VAc)为主单体,丙烯酸(AA)为改性功能单体,以半连续加料方式进行无皂乳液共聚过程,得到了稳定且固含量为30%左右的乳液。
Reaction Mechanism and Characterization of In-situ Soap Free Emulsion Polymerization of Wollastonite-g-PMMA
原位无皂乳液聚合硅灰石接枝PMMA反应机理及表征
Carboxylated styrene butadiene latex for carpet backing was synthesized by using soap-free (emulsifier concentration being below the critical micell concentration) and high temperature emulsion polymerization pro-cess.
本工作采用无皂(乳化剂浓度在其临界胶束浓度以下)、高温乳液聚合工艺合成了地毯二次背衬用羧基丁苯胚乳。
A appropriate amount of reactive polyurethane emulsifier (URE) is added into a soap-free emulsion system prepared with methyl methacrylate and butyl acrylate. The influence of monomer ratio and organic solvents on the emulsion film and the stability of emulsion are investigated.
在甲基丙烯酸甲酯和丙烯酸丁酯的无皂乳液体系中,加入适量的自制聚氨酯型反应性乳化剂(URE),考察单体配比和有机溶剂对乳胶膜性能的影响,并研究了聚合物乳液的稳定性。
A curable emulsion of Ca 2 +/acrylate copolymer soap free hydrosol was prepared. Some factors which affected coating properties such as curing temperature, content of crosslinker were studied.
研究了Ca2+/聚丙烯酸酯无皂水溶胶交联乳液的制备条件,考察了交联温度、交联剂用量对涂膜性能的影响。
Study on cement mortar modified by vac/dmc soap-free cationic emulsion copolymerization
VAC/DMC阳离子无皂乳液改性水泥砂浆研究
The Preparation of Core-Shell Structure Composite Particles by Semi-Continuous Soap-Free Emulsion Polymerization
半连续无皂乳液聚合制备核壳结构复合粒子的研究
Application of Reactive Emulsifier in Soap-free Silica Sol Styrene-Acrylate Emulsion Polymerization
反应性乳化剂在无皂硅溶胶苯丙乳液聚合中的应用