Feldspar: a solvent raw material, billets in the ceramics for daily use to play the role of solvents, billets in the quartz, clay minerals have a high melting point, while the feldspar in the 1000 - 1200 ℃ melt feldspar dissolved to form, at high temperature to dissolve part of the decomposition of kaolinite and quartz particles, help to reduce the firing temperature and speed into the Tao reaction to allow the ceramic billet tends to compact, high temperature feldspar melt has a certain viscosity, to prevent embryo temperature deformation, the melt formed after cooling the glass phase can improve the transmittance of products, in addition to long barren rock is also a drying agent can reduce the green body shrinkage, reducing drying deformation, shortening contraction time.
长石：是一种溶剂原料，在日用陶瓷坯料中起溶剂作用，坯料中的石英、粘土矿物质都有很高的熔点，而长石在1000--1200℃溶解形成长石熔体，在高温下能溶解部分高岭石分解物和石英颗粒，有助于降低烧成温度和加快成陶反应的进行，使陶坯趋于致密，高温下长石熔体具有一定的黏度，能防止胚体高温变形，熔体冷却后形成的玻璃相能提高制品的透光性，此外长石也是一种瘠化剂可降低坯体干燥收缩，减少干燥变形，缩短收缩时间。
They are cement, quartz, feldspar, calcite, gypsum, limestone, dolomite, graphite, fluorite, aedelforsite, phosphate ore, fused calciummagnesium phosphate, carbamide, electrolytic manganese metal, ferromanganese, coal, gangue, slag, zirconium, steatite, granite, orthoclase, marble, barytes, ceramics, glass, etc.
例如水泥、石英、长石、方解石、石膏、石灰石、白云石、石墨、萤石、硅灰石、磷矿石、钙镁磷肥、煤、煤矸石、矿渣、锆英砂、滑石、花岗岩、钾长石、大理石、重晶石、陶瓷、玻璃等千余种物料粉磨加工。
On the basis of feldspar ceramics, adding more albite, firing temperature of domestic fine pottery are depressed to 1230 ℃ and firing time are depressed to 2 hours. Product Quality accords with national standard GB/T3532-1995 (domestic fine pottery).
作者在长石瓷的基础上，引入多量的钠长石，将日用细瓷的烧成温度降低到1230℃烧成周期缩短为2小时，产品质量符合GB／T3532-1995《日用瓷器》国家标准。
Therefore, the ammonia leaching residue can be used as the fluxing agent and pigment in quartz-feldspar-kaolin ternary system ceramics.
研究认为，氨浸渣可以作为石英-长石-高岭土3组分陶瓷的助熔剂和色料。