Such raw materials as waste polyethylent cable particles, pure polyvinyl chloride powder, wood powder, a metallic soap stabilizer, a coupling agent, chlorinated polyethylene and methacrylic acid polyesters and a lubricator are added into and mixed in a high speed mixer according to the formula, and the mixing temperature is 100 to 110 DEG C, the mixing time is 20 to 35 min; the well mixed material is added into an extruder for extrusion, the rotating speed of the mainframe of the extruder is 40 to 60r/min, the rotating speed of a feeding machine is 4 to 6r/min, and the materials are shaped after being extruded.
将废旧聚氯乙烯电缆颗粒、纯聚氯乙烯粉、木粉、金属皂类稳定剂、偶联剂、氯化聚乙烯、甲基丙烯酸多元酯、润滑剂按照配方配制的原料加入高混机中混合，混合温度为100℃～110℃，混合时间为20～35分钟；将混合好的原料加入挤出机中进行挤出，挤出机主机转速为：40～60转/分钟，喂料机转速为：4～6转/分钟；挤出后进行定型。