The hull is made from an phenol novolac epoxy resin, with a fiberglass reinforcement.
船体是由一苯酚酚醛环氧树脂，与玻璃纤维加固。
Electrochemical impedance spectra were measured for the aluminum electrodes coated and uncoated with an epoxy cresol novolac film in 0.5mol·dm^-^3 NaCl solution (60℃) at open circuit petential, respectively.
本工作测量了覆盖环氧膜的铝电极在NaCl溶液中的电化学阻抗谱，并求得了该膜的膜电阻、膜电容和环氧膜与底金属间的腐蚀电阻及双电层电容。
Phenol novolac resins and sulphanilamide were used to cure rigid rod epoxy resins, namely DGEBP, DGETMBP and traditional epoxy resin.
用线性酚醛树脂和4-氨基苯基氨基砜作为固化剂，与刚性棒状环氧树脂联苯环氧、四甲基联苯环氧和传统双酚A环氧树脂分别进行固化。
The actinic radiation-curable and cationically polymerizable organic substance is at least one glycidylether of a polyhydric aliphatic, alicyclic or aromatic alcohol having at least three epoxy groups with epoxy equivalent weight between 90 and 800 grams per equivalent, at least one solid or liquid alicyclic epoxide with an epoxy equivalent weight between 90 and 330 grams per equivalent having at least two epoxy groups and monomer purity greater than about 90% by weight, or at least a solid or liquid epoxycresol novolac or epoxyphenol novolac having epoxy equivalent weight between 130 and 350, or mixtures thereof.
可光化辐射固化并可阳离子聚合的有机物质为至少一种带有至少3个环氧基团环氧当量为90―800克每当量的脂族、脂环族或芳族多元醇的缩水甘油醚，至少一种环氧当量为80―330克每当量带有至少两个环氧基团且单体纯度大于约90wt％的固态或液态脂环环氧化物，或至少一种环氧当量为130―350的固态或液态环氧甲酚线性酚醛清漆或环氧苯酚线性酚醛清漆，或其混合物。
By using acrylic acid to modify the F-51 novolac epoxy resin, novolac epoxy acrylate with photosensitive character can be synthesized, which is then induct the carboxyl groups in its molecular chain for good ability of alkali developable by using maleic anhydride.
采用丙烯酸类单体改性F51型酚醛环氧树脂的方法，合成具有光固化特性的酚醛环氧丙烯酸酯树脂，再用马来酸酐进行改性，在分子链上引入羧基，使树脂具有良好的碱溶性。
It was found that novolac epoxy resin and TPP had excellent synergistic effects on the flame retardancy of ABS.
研究了环氧树脂种类、各组分配比及用垫等对ABS的阻燃性能及力学性能的影响。
The friction coefficient of novolac epoxy-graphite composite was affected by the size of graphite.
实验中还发现，提高活性稀释剂的含量在增强固化物韧性的同时不会明显增大固化物的摩擦系数。
In the investigation, novolac epoxy resin and graphite were employed to product a coating in order to decrease the friction coefficient of tubular screw.
研究中采用环氧树脂和石墨粉制备了密封涂层，研究了涂层的摩擦、磨损特性与有关的制备工艺和配方之间的关系。
A kind of polyamine curing epoxy novolac chelating resin has been synthesized through the reaction between F_ (44) and polyamine. Factors affecting the adsorption properties such as pH value, temperature, concentration of Cu~(2 +) are studied.
环氧酚醛树脂（F44）经多胺交联固化得到了胺固化酚醛型螯合树脂，测定了该树脂在不同温度、浓度、pH值等条件下对铜离子的吸附性能。
A co-cure method of novolac epoxy resin (F-51) and diallyl isophthalate (DAIP) were used to enhance the heat resistance of epoxy resins.
采用共固化的方法，得到酚醛环氧树脂（F-51）和间苯二甲酸二烯丙基酯（DAIP）的共固化树脂。
The Effect of Different Percent of Silicone Resin on Properties of Modified Novolac Epoxy Coating
有机硅含量对改性酚醛环氧树脂涂料性能的影响
The novolac & type epoxy resin modified with novolac, reinforced with glass fiber, cured with proper curing system, was used for preparing molding compound. This material has good combination properties, especially processability, and can be used as grade F insulating material.
以线型酚醛树脂改性酚醛型环氧树脂，再用玻璃纤维增强，并采用合适的固化体系，所得的增强塑料，综合性能优良，成型工艺性好，可作为F级绝缘材料使用。
Recent development of O cresol novolac epoxy resin
邻甲酚甲醛环氧树脂的最新进展
During the curing reaction, ester groups were intramolecularly transferred from the esterified phenol novolac resin to the o - cresol novolac epoxy resin.
结果表明，在促进剂2甲基咪唑存在下活性酯固化邻甲酚环氧树脂的反应是通过分子内机理进行的。
Structure and properties of novolac cyanate ester co-cured with epoxy resins
酚醛氰酸酯/环氧共固化树脂的结构和性能
The Development of J-91 Heat Resistant Epoxy Novolac Adhesive Studies on Reaction Kinetics of o-Cresol Novolac Resin Using Phenol Novolac Acetate as Curing Agent by FTIR
J－91耐热性环氧化酚醛胶粘剂的研制FTIR法研究乙酸酚醛酯固化邻甲酚环氧树脂的反应动力学
Preparation and properties of fluorinated p-phenyl-type novolac epoxy resins
含氟对苯型酚醛环氧树脂的制备与性能研究
Synthesis and Application of Photosensitive Novolac Epoxy Acrylate Resins
酚醛环氧丙烯酸光敏树脂的合成及应用
Study on curing process of o-cresol novolac epoxy resin system
邻甲酚甲醛环氧树脂固化体系的研究
Effects of hydrothermal ageing on structures and properties of cyanate/epoxy novolac blends
湿热老化对氰酸酯树脂/酚醛环氧树脂共混物结构与性能的影响