To tie in with the ceramics factory, furniture, technology, lighting, toys, hardware and electronics industry development, the main production of styrofoam sheets, plates, free-forming products, Zhenzhu Mian (membrane, sheet, Bags, tubing, bar, contoured wood) bubble paper; LLDPE stretch film, sheet metal hollow, hollow boxes, pearl-and sponge, desiccant, PVC plastic boxes, etc. All kinds of packaging materials products.
本厂为配合陶瓷、家私、工艺、灯饰、玩具、五金电子等行业发展的需要，主要生产发泡胶片材、板材、免模成型制品，珍珠棉（卷材、片材、袋子、管材、棒材、异形材）汽泡纸；LLDPE拉伸膜，中空板材，中空箱、珍珠板以及海棉，干燥剂、PVC吸塑盒等各种包装材料制品。
Results indicate that the optimal HDPE and LLDPE proportion is 70 to 30; the practical molding time is 15 minutes and molding temperature is 290℃; the part thickness is 6 mm, and the close parallel walls, the fillet radius of inner surface and outer surface is 18 mm, 3.2 mm and 6.5 mm respectively; the material of the mold is aluminum.
结果表明：LLDPE/HDPE=70：30可作为滚塑成型原料；最佳成型时间15min，最佳成型温度290℃；制件壁厚为6mm，近距平行壁距离为3倍壁厚，圆角处内表面半径为6.5mm，外表面半径为3.2mm，加强筋采用高度较小的多条平式加强筋；模具为铸铝合金材质。
The black linear low density polyethylene cable jacket material was prepared by using a kind of basic resin named LLDPE X produced by Yangzi Petrochemical Co.
采用扬子石化公司生产的LLDPE X基体树脂制备通信电缆用黑色LLDPE电缆护套料，研究了电缆护套料各组分选择、用量和加工工艺对其性能的影响，给出了成型电缆护套的工艺条件。
At first this paper discussed the property of LLDPE and the effect of temperature and MI to the torsion melt-flow.
本文首先讨论了LLDPE的基本性质及温度和熔融指数对LLDPE的转矩流变值的影响。
Since the company has committed to have the import and export of plastic packaging supplies business, Main products for a variety of HDPE, LDPE, LLDPE Series of reusable shopping bags, even the volume vest bag, even the volume discount for each purchase of vests bags, calendars vest bag, food bag, frozen bags, side seal bags, C-FOLD bag, color printing bag, rope wear trash bags, ice bags, aprons bags, diaper bags, such as hundreds of varieties of plastic packaging products.
公司创办以来便致力于塑料包装用品的进出口业务，主营产品为各种HDPE、LDPE、LLDPE系列环保购物袋、连卷背心袋、八折连卷背心袋、挂历背心袋、食品袋、冷冻袋、边封袋、C-FOLD袋、彩印袋、穿绳垃圾袋、冰块袋、围裙袋、尿布袋等上百个品种的塑料包装制品。
Process for the preparation of LLDPE with improved processability by gas phase polymerization performed in two or more reactors, wherein, whatever the order, in one of the reactors a mixture of ethylene and an alpha-olefin CH2=CHR, where R is an alkyl having 1-10 carbon atoms, is polymerized to yield a copolymer containing up to about 20% by mole of the alpha-olefin, and in another reactor a mixture of propylene and an alpha-olefin CH2=CHR'(where R'is an alkyl having 2-10 carbon atoms), is polymerized to yield a copolymer containing from 5 to 40% by weight of said olefin, in an amount of 5-30% with respect to the total polymer weight and the polymer-catalyst system obtained in the first reactor is fed to the other reactors.
在二个或更多反应器进行气相聚合制备改进加工性的LLDPE的方法，在一个反应器中，聚合乙烯和α－烯烃CH2=CHR其中R是1―10个碳原子的烷基）的混合物产生含有高达大约20％的α－烯烃的共聚物，和在另一个反应器中，聚合丙烯和α－烯烃CH2＝CHR'(其中R'是2―10个碳原子的烷基）产生含有5―40％所述烯烃的共聚物，其量为总聚合物重量的5―30％，在第一反应器中得到的聚合物―催化剂体系送入另一个反应器中。
It was found that the mechanical property of Z-N LLDPE can be improved after the treatment of thermal segregation.
由于聚乙烯的通用性和较高的市场占有率，数十年来已被广泛研究。
We are the factory of the LLDPE stretch film at China mainland.
例句1。我们是工厂的线型低密度聚乙烯拉伸膜在中国大陆。
The influence of nano-SiO〓 content on the dynamic mechanical properties of LLDPE composites was also studied.
同时，研究了硅烷偶联剂/分散剂复配进行纳米SiO〓表面处理的方法与分散稳定机理。
Taking LLDPE whole process simulation as an example, analyzes and discusses the application of Aspen Plus software.
以LLDPE装置全流程模拟为例，对应用Aspen Plus软件进行分析和讨论。
The results show that ASO could improve the flame retardancy and the performance of smoke suppression of LLDPE.
结果表明：ASO提高了阻燃性能和抑烟效果。
Based on this background, basic theoretical research and the utility of LLDPE should be increasingly considered.
对LLDPE的改性研究除了有机共混改性之外，还可利用无机填料进行改性。
Required film is a hexene LLDPE and LDPE product that possesses good puncture and impact resistance.
需要的薄膜是具有好的抗挤压的己烷低密度聚乙烯及低密度聚乙烯产品。
Standard adjustment degree and level of adjusting weights of state variable weights vector are introduced.
通过调节两种催化剂之间的比例和MAO的用量制备了一系列支化度不同的LLDPE产品。
In the course of friction and wear, the debris produced by M-UHMWPE and LLDPE transfer to the worn surface exits in the contact surface, which act as anti-friction and wear-resisting agent.
在摩擦过程四川大学褚项I学位论文中，M一UHMwPE和LLDPE向磨擦界面转移产生的磨屑分布于摩擦界面，起到了减摩耐磨剂的作用。
The LLDPE speciality resin BD used in drip irrigation tube was developed by adding peroxide to extruder.
通过在挤出机中添加过氧化物的方法，成功地在LLDPE装置上生产出滴灌管专用料，并提出了生产滴灌管专用料的典型配方和工艺参数。
Jafari S H%Yavari A%Asadinezhad A Correlation of Morphology and Rheological Response of Interfacially Modified PTT/m-LLDPE Blends with Varying Extent of Modification POLYMER, 2005, 14
何曼君%陈孝维%董西侠高分子物理上海：复旦大学出版社，2000，席世平%窦仕臣%陈江接枝PP/PET共混物的结构与性能工程塑料应用，1997，06
The flow properties of linear low density and low density polyethylene blend under the extrusion conditions were investigated with capillary rheometry.
LLDPE为新一代聚乙烯，其制品在存放及使用过程中显示出一些突出的特点，如优异的机械强度、耐环境应力开裂性、耐热性、耐寒睦和抗翘曲性等。
At the same time, the response current measurements of LLDPE/SiC composite and the plate of controlling electric field stress under the excitement of trapezoidal wave are carried out using this measurement system, and the results are discussed.
与此同时完成了对SiC颗粒掺杂的LLDPE片状试样以及电场应力控制片在梯形波激励下的响应电流的测试，并对测试结果进行了初步分析。
The results show that the PTC intensity of HDPE/CB composite is the highest (about 10〓) and the temperature switching property is the best of the three.
以三种聚乙烯(LDPE、LLDPE和HDPE)为基材，研究其结构对复合材料PTC强度，温度开关特性及热稳定性等的影响。